Measures to Prevent and Control Deformation Caused by Welding

  • Posted: 11/29/2022 10:11:48
  • Hits: 14

3.1 Welding sequences In view of the above structural characteristics of welding flanges and cylinders, when compiling the welding process, we can skillfully use the welding stress of the material to make it as far as possible to offset each other in the direction of action, as shown in Figure 3. The...


Deformation of Stainless Steel Slip-on Flanges After Welding

  • Posted: 11/07/2022 08:11:17
  • Hits: 32

In the manufacturing process of pressure vessels, due to the unbalanced heating of the workpiece in the welding process and the cooling after welding, welding stress will occur inside the workpiece. Residual deformation will easily happen after welding if effective preventive and control measures are...


Controlling Deformation of Slip-on Flanges with Large Diameters

  • Posted: 10/08/2022 03:10:46
  • Hits: 12

A batch of flanges for ethylene engineering are manufactured in a factory recently. There are some problems in the manufacturing process. One of the prominent problems is how to control the deformation of slip-on flanges with large diameters during assembly.   This batch of slip-on flanges has...


The Analysis of Causes of Cracking of Austenitic Stainless Steel Flanges

  • Posted: 06/28/2022 09:06:20
  • Hits: 21

1. Comprehensive analysis Combined with the above physical and chemical test results and operating conditions of the flange, the following analyses are carried out. (1) Sensitive materials There are a lot of precipitates on the grain boundaries of the flange microstructure, and the production of...


Physical and Chemical Inspection of Cracking of Austenitic Stainless Steel Flanges

  • Posted: 06/09/2022 11:06:28
  • Hits: 14

During the production and operation of a chemical plant, it was found that there was a leakage in the flange neck. After observation, it was found that there were cracks in the flange neck along the circumferential direction, as shown in Figure 1. The internal medium of this flange is aviation kerosene....


Simulation Tests of Failures Caused by Pickling Corrosion of SS Flanges

  • Posted: 04/22/2022 09:04:43
  • Hits: 8

1. Welding simulation tests Austenitic stainless steel has excellent corrosion resistance, but carbide aggregates at the grain boundary at the welding seam part, especially the heat-affected zone in actual production. Finally, intergranular corrosion occurs due to the corrosive medium. Therefore, to...


Electric Arc Materials Adding for Nuclear Grade Flanges (Part Two)

  • Posted: 02/10/2022 08:02:12
  • Hits: 12

(2) Microstructure After the arc additive TIG surfacing of the flange simulation part is completed, the metallographic samples are ground from the fusion line and the center of the surfacing layer respectively, and they are etched with ferric chloride plus hydrochloric acid solution. Observe...


Electric Arc Materials Adding for Nuclear Grade Flanges (Part One)

  • Posted: 01/27/2022 08:01:51
  • Hits: 14

Abstract: According to the corrosion status of the flange surface of a certain pipe end of a nuclear power plant and the site construction conditions, the method of arc materials adding of the flange surface was studied. Through the demonstration and analysis of the arc surfacing test of the...


The Calculation of the Flange Under the Internal Pressure and External Load

  • Posted: 11/13/2021 08:11:32
  • Hits: 1157

Abstract: In the design and manufacture process of the pressure vessel, the selection and design calculation of flanges have always been an unavoidable important content. Flanges for pressure vessels (forced sealing flanges) are often subjected to not only internal pressure but also axial...